| Purethane® AR | |
| Solvent Borne, Modified Polyurethane Primer | |
| GENERIC TYPE : | Two Component Polyurethane |
| USAGE : | Steel Substrates |
| COMPOSITION: | |
| Resin | Activator |
|
Modified Polyol ,Color Pigments, Aromatic Solvents, Additives |
Modified Polymeric Di-Isocyanate |
| SPECIFICATION : | |
| Mixing Ratio : | Resin / Activator = 4 : 1 ( Weight ) |
| Thinning Ratio : | 0- 20% with xylene if required. |
| Colour : | Resin : Reddish Brown , Activator : Brown |
| S.G at 20oC | 1.1 ( Resin 1.07, Activator 1.24 ) |
| Viscosity at 20oC | Resin 700 mPa, Activator 300 mPa |
| Pot Life at 20oC | 2-3 Hours |
| Touch Dry at 20oC | 1-2 Hour |
| APPLICATION STANDARD : | |
| Surface Preparation : | |
|
Abrasive blast to near white in accordance with SSPC-SP10 using granulated copper slag or similar abrasive to obtain an anchor pattern of 75- 100 microns. |
|
| Conditions : | |
| Temperature | 5 - 45oC |
| Humidity | Under 90% R.H |
| Surface Temperature | 3oC higher than dew point |
| Application Method : | Air Spray, Airless Spray (One Component) , Brushing |
| Film Thickness : | 20 - 40 Microns DFT |
| Theoretical Coverage : | 54 gms. / Sq. Metre |
| Overcoat Interval : | Below 10oC - Upto 72 Hours |
|
Below 25oC - Upto 48 Hours |
|
| Below 35oC - Upto 24 Hours | |
| Below 45oC - Upto 12 Hours | |
| PRECAUTIONS : | |
| Use in conditions of adequate ventilation. Keep away from heat and open flame | |